1. After applying for a period of time, it was found that the trajectory of the guide rail was imprinted and the steel ball of the slider broke. What is the reason for this?

The main factor is the load, which causes the steel ball to break off its trajectory, resulting in sustained damage to the trajectory. You can use the replacement of one level larger sliders, increase the number of sliders, reduce external loads, and change device techniques to reduce unilateral force situations. If the reason is due to the smooth surface, you can try applying another type of smooth oil, adding the amount of smooth oil, and reducing the smooth interval. Request to frequently check for foreign object intrusion, and if there is foreign object intrusion, improve the sealing accessories.

2. Why do steel balls fall out and detach after a period of time when the slider is applied?

The detachment of the iron pin from the bead groove causes damage to the steel ball and the end of its service life, resulting in fatigue and excessive loading on the surface of the steel component. This may be due to excessive loading, incorrect installation, or one-sided stress.

3. After walking the slider for a period of time, do you notice any deformation or breakage of the end cap and end anti fouling?

Errors in the installation method may result in only one side of force being applied between the slider and the track, or may cause deformation or rupture of the end cap and end anti fouling due to external forces. If there are internal defects in the slider, the anti fouling system can be changed to improve the smoothness of the oil, add the amount of smoothness oil, and reduce the interval between smoothness times. When installing, attention should be paid to the difficulty of adjusting the device angle. To improve the product equipment, it is required that the master install it to avoid damaging the slide rail slider.